Publicaciones en colaboración con investigadores/as de Universidad de Burgos (12)

2021

  1. Fracture toughness of coarse-grain heat affected zone of quenched and tempered CrMo steels with internal hydrogen: Fracture micromechanisms

    Engineering Fracture Mechanics, Vol. 241

  2. Influence of non-homogeneous microstructure on hydrogen diffusion and trapping simulations near a crack tip in a welded joint

    Theoretical and Applied Fracture Mechanics, Vol. 112

2020

  1. SPT analysis of hydrogen embrittlement in CrMoV welds

    Theoretical and Applied Fracture Mechanics, Vol. 110

2016

  1. Application of the miniature small punch test for the mechanical characterization of polymer materials

    Theoretical and Applied Fracture Mechanics, Vol. 86, pp. 78-83

  2. Determination of the creep crack initiation properties using pre-cracked small punch tests

    Theoretical and Applied Fracture Mechanics, Vol. 86, pp. 39-44

  3. Effect of hydrogen embrittlement on the tensile properties of CrMoV steels by means of the small punch test

    Materials Science and Engineering A, Vol. 664, pp. 165-176

  4. Mechanical behavior and failure analysis of recycled polymers by use of miniature punch specimens

    Journal of Applied Polymer Science, Vol. 133, Núm. 4

2015

  1. Development of a new methodology for estimating the CTOD of structural steels using the small punch test

    Engineering Failure Analysis, Vol. 50, pp. 88-99

  2. Effect of confinement level on mechanical behaviour using the small punch test

    Engineering Failure Analysis, Vol. 58, pp. 206-211

  3. Influence of the notch shape of pre-notched small punch specimens on the creep failure time

    Engineering Failure Analysis, Vol. 56, pp. 332-337

2011

  1. Analysis of different techniques for obtaining pre-cracked/notched small punch test specimens

    Engineering Failure Analysis, Vol. 18, Núm. 8, pp. 2282-2287

2009

  1. Inverse determination of the elastoplastic and damage parameters on small punch tests

    Fatigue and Fracture of Engineering Materials and Structures, Vol. 32, Núm. 11, pp. 872-885